Kapton® FWN magnet wire insulation
Kapton® FWN is ideal for demanding magnet wire applications and for difficult-to-wind motors.
Kapton® FWN is a multi-layer polyimide & fluoropolymer dispersion-coated film. The fluoropolymer coating functions as a heat-fusible layer for bonding to magnet wire conductors. It has superior scrape abrasion resistance and exhibits lower frictional properties than wire insulated with other commonly used polyimide materials. Kapton® FWN is ideal for demanding magnet wire applications and for difficult-to-wind motors.
- Magnet wire
- Traction motors used in rail, auto, and mining
- Industrial motor insulation
- Wind, hydro generators
|Thickness, mil||1.30||1.50||ASTM D374|
|Tensile Strength, kpsi (MPa)||30 (207)||27 (186)||ASTM D882|
|Elongation, %||92||87||ASTM D882|
|Dielectric Strength, V/mil||6400||4700||ASTM D149|
Product Data Sheets (2)
RELATED DUPONT PRODUCTS & SERVICES
DuPont™ Kapton® B polyimide film exhibits an excellent balance of physical, chemical, and electrical properties over a wide temperature range, with superior dimensional stability at elevated temperatures.
Kapton® FCRC combines corona resistant polyimide film with a heat fusible FEP fluoropolymer film. The corona resistance provides improved service life and operational efficiencies vs conventional insulation materials.
Kapton® corona resistant film withstands the damaging effects of corona discharge. The corona resistance provides improved service life and operational efficiencies versus conventional insulation materials.
DuPont™ Kapton® FN is a general purpose HN film that is coated or laminated on one or both sides with Teflon® FEP fluoropolymer.
Kapton® polyimide film is widely used as a dielectric substrate for its high temperature resistance, self extinguishing burn characteristics, toughness and flexibility.
DuPont™ Kapton® MT polyimide film is a homogeneous film possessing 3x the thermal conductivity and cut through strength of standard Kapton® HN.
Kapton® HN is the recommended choice for applications that require an all-polyimide film with an excellent balance of properties over a wide range of temperatures.
Kapton® GS film has been specifically designed and manufactured to expand the processing window and improve yields during artificial graphite sheet production.
In applications where low shrinkage and superior adhesion are important, Kapton® HPP-ST is the polyimide film of choice.
DuPont™ Kapton® FPC polyimide film is treated on both sides with excellent balance of physical, chemical and electrical properties over a wide temperature range.
Kapton® FCR is a state-of-the-art wire insulation that will withstand corona discharge while delivering improved long term performance, cost effectively.
DuPont Kapton® CR polyimide film was developed specifically to withstand the damaging effects of “corona,” which can cause ionization and eventual breakdown of an insulation material or system when the voltage stress reaches a critical level.