Kapton® FWN is ideal for demanding magnet wire applications and for difficult-to-wind motors. Kapton® FWN is a multi-layer polyimide & fluoropolymer dispersion-coated film. The fluoropolymer coating functions as a heat-fusible layer for bonding to magnet wire conductors. It has superior scrape abrasion resistance and exhibits lower frictional properties than wire insulated with other commonly used polyimide materials. Kapton® FWN is ideal for demanding magnet wire applications and for difficult-to-wind motors.
DuPont™ Kapton® 150FWN019 is a two-layer, polyimide, FEP fluoropolymer dispersion-coated heat-fusible composite film with a unique balance of excellent physical, electrical, thermal durability and chemical resistance properties. 150FWN019 has superior scrape abrasion resistance and motor manuacturers have reported that wire insulated with 150FWN019 exhibits lower frictional properties than wire insulated with other commonly used polyimide materials. 150FWN019 is ideal for demanding magnet wire applications. and for difficult-to-wind motors.
|
|
| Gross Weight | Net Weight | Carton Each | Carton Length | Carton Weight | Carton Height |
|---|---|---|---|---|---|
| 4696 | 0 | 0 | 0 | ||
| 4423 | 0 | 0 | 0 | ||
| 5669 | 0 | 0 | 0 |
| Property | Method | Unit | Value |
|---|---|---|---|
| Hydroscopic Coefficient of Expansion | DuPont Test Method | ppm/%RH | <12 |
| Water Vapor Permeability (kptn-127) | ASTM E-96 | gms/m2 /day | <10 |
| Moisture Absorption @ 100%RH | ASTM D-570 (kptn-31) | % | <2.2 |
| Property | Method | Unit | Value |
|---|---|---|---|
| Tensile Modulus (kptn-99) | ASTM D-882 | Kpsi/Gpa | |
| Tensile Strength (kptn-103) | ASTM D-882 | Kpsi/Mpa | 17.3/119 |
| Elongation to break | ASTM D-882 | % | 55 |
| Thickness (kptn-111) | DuPont Test Method | mils/microns | 1.50/38 |
| Specific Gravity (kptn-84) | ASTM D-1505-90 | gms/cc | 1.68 |
| Property | Method | Unit | Value |
|---|---|---|---|
| Dielectric Strength (kptn-19) | ASTM D-149 (kptn-5) | V/mil (kV/mm) | >3600 (>142) |
| Dielectric Constant | ASTM D-150 (kptn-10) | 1Khz | <3.0 |
| Volume Resistivity (kptn-120) | IPC-TM-650 | ohm-cm | >10 E16 |
| Dissipation Factor at 1 kHz | ASTM D-150 (kptn-10) | — | <0.002 |
| Property | Method | Unit | Value |
|---|---|---|---|
| Minimum Heat Seal Strength (FEP to FEP) | DuPont Test Method | gms/cm | >235 |
| Minimum Heat Seal Strength (FEP to Kapton®) | DuPont Test Method | gms/cm | >235 |
|
Fabric/material |
COATED FILM |
|---|---|
|
Design |
150FWN019 |
|
Seam |
NON-OASIS COATED |
|
Packaging |
150FWN019 |
|
Hazard |
|
|
Coated Material |
HPF FLM SF&FP |
|
Features |
COATED FILMS |