DuPont™ Kapton® 150PRN411 is ideal for insulating copper conductor used in high temperature magnet wire applications. It is a multi-layer heat-fusible composite film that enables higher operational temperature functionality and improved abrasion resistance. 150PRN411 consists of a layer of 25 micron thick Kapton® HN polyimide film between two layers of high melt temperature fluoropolymer. One of the fluoropolymer layers is approximately ten microns thick and the other layer is approximately three microns thick.
The properties of DuPont™ Kapton® 150PRN411 make it suitable for insulating copper conductor used in high temperature magnet wire applications where improved adhesion between layers and abrasion resistance are desired. Kapton® 150PRN411 polyimide film consists of a layer of 25 micron thick Kapton® HN polyimide film between two layers of high melt temperature fluoropolymer. One of the fluoropolymer layers is approximately ten microns thick and the second layer is approximately three microns thick.
| Gross Weight | Net Weight | Carton Each | Carton Length | Carton Weight | Carton Height |
|---|---|---|---|---|---|
| 3934 | 0 | 0 | 0 |
| Property | Method | Unit | Value |
|---|---|---|---|
| Flammability (kptn-29) | UL Test Method | UL-94 | V-0 |
| Yield | — (kptn-1) | ft2 /lb | 78.4 |
| — (kptn-1) | m2 /kg | 16 | |
| UL Mechanical RTI | UL 746B | °C | 200 |
| Thickness (kptn-111) | ASTM D-374 | µm | 38 |
| ASTM D-374 | mil | 1.5 | |
| UL Electrical RTI | UL 746B | °C | 240 |
| Elongation (kptn-22) | ASTM D-882 | % | 88 |
| 350°C Heat Seal Strength (F to Cu) | DuPont Test Method | gms/cm | 366 |
| DuPont Test Method | gms/in | 930 | |
| Tensile Strength (kptn-103) | ASTM D-882 | MPa | 186 |
| ASTM D-882 | kpsi | 27 | |
| Tensile Modulus (kptn-99) | ASTM D-882 | kpsi | 310 |
| ASTM D-882 | GPa | 2.14 | |
| Dissipation Factor at 1 kHz | ASTM D-150 (kptn-10) | — | 0.002 |
| Dielectric Strength (kptn-19) | ASTM D-149 (kptn-5) | V/mil | 5400 |
| ASTM D-149 (kptn-5) | kV/mm | 212 | |
| Volume Resistivity (kptn-120) | ASTM D-257 (kptn-21) | ohm-cm | >1016 |
| Density (kptn-17) | ASTM D-1505 | g/cc | 1.68 |
| Dielectric Constant | ASTM D-150 (kptn-10) | — | 3.4 |
|
Fabric/material |
COATED FILM |
|---|---|
|
Design |
150PRN411 |
|
Seam |
NON-OASIS COATED |
|
Packaging |
150PRN411 |
|
Hazard |
|
|
Coated Material |
HPF FLM SF&FP |
|
Features |
COATED FILMS |