Kalrez® perfluoroelastomer parts provide best in class chemical resistance for exploration and production services while also meeting the industry standard requirements.
Chemical resistance |
|
Broad temperature capability |
|
Gross Weight | Net Weight | Carton Each | Carton Length | Carton Weight | Carton Height |
---|---|---|---|---|---|
0 | 0 | 0 | |||
0 | 0 | 0 | |||
0 | 0 | 0 |
Property | Value | Unit | Method |
---|---|---|---|
NORSOK M-710 (Rev. 2) Certified | Size(AS568 size 312),Cross Section diameter(5.33 mm, nominal (size 312)), Groove fill(67%, nominal) | — | 10 cycles, one every 24 h |
TOTAL GS EP PVV 142 (Rev. 5) Qualified | Size(AS568 size 349, and size 425),Cross Section diameter(5.33 mm, nominal (size 349); 6.99 mm nominal (size 425)), Groove fill(73%, nominal) | — | 5 cycles |
Property | Value | Unit | Method |
---|---|---|---|
Hardness | ASTM D2240 (Pellet test specimens) | Durometer, Shore A | 95 |
Compression Set, 70 hrs.at 204 °C (400 °F) | ASTM D395B & D1414, (AS568 K214 O-ring test specimens) | % | 33 |
ASTM D395B, (Pellet test specimens) | % | 19 | |
Maximum Service Temperature | DuPont proprietary test method; performance will vary with seal design and application specifics | °C (°F) | 250 (482) |
Elongation at Break | ASTM D412 (Dumbbell test specimens) | % | 80 |
50% Modulus | ASTM D412 (Dumbbell test specimens) | MPa (psi) | 14.18 (2057) |
Color | - | — | Black |
Tensile Strength at Break | ASTM D412 (Dumbbell test specimens) | MPa (psi) | 19.49 (2827) |
Lowest Service Temperature, Tr10 | ASTM D1329 (ISO 2781) (slab test specimens) | °C (°F) | –7.4 (18.68) |
Lowest Service Temperature | DuPont proprietary test method; performance will vary with seal design and application specifics | °C (°F) | –21 (–5.8) |
Lowest Service Temperature, Tg | DuPont proprietary test method (DSC midpoint) | °C (°F) | –1 (30.2) |