Kalrez® perfluoroelastomer parts provide best in class chemical resistance for exploration and production services while also meeting the industry standard requirements.
| Gross Weight | Net Weight | Carton Each | Carton Length | Carton Weight | Carton Height |
|---|---|---|---|---|---|
| 0 | 0 | 0 | |||
| 0 | 0 | 0 | |||
| 0 | 0 | 0 |
| Property | Value | Unit | Method |
|---|---|---|---|
| Hardness | ASTM D2240 (Pellet test specimens) | Shore A | 74 |
| Compression Set, 70 hr. at 204 °C (400 °F) | ASTM D395B & D1414, (AS568 K214 O-ring test specimens) | % | 15 |
| ASTM D395B, (Pellet test specimens) | % | 11 | |
| 100% Modulus | ASTM D412 (Dumbbell test specimens) | MPa (psi) | 9.01 (1307) |
| Elongation at Break | ASTM D412 (Dumbbell test specimens) | % | 195 |
| Tensile Strength at Break | ASTM D412 (Dumbbell test specimens) | MPa (psi) | 18.32 (2657) |
| Maximum Service Temperature | DuPont proprietary test method; performance will vary with seal design and application specifics | °C (°F) | 300 (572) |
| Color | - | — | Black |
|
Fabric/material |
CBS 6190LS |
|---|---|
|
Design |
6190LS |
|
Seam |
6190LS |
|
Packaging |
6190LS |
|
Hazard |
|
|
Coated Material |
CBS 6190LS |
|
Features |
CUSTOM BLACK SHAPE |
|
Color |
BLACK |