Kalrez® perfluoroelastomer parts provide best in class chemical resistance for exploration and production services while also meeting the industry standard requirements.
| Kalrez® Spectrum™ 7275 seals allowed to extend the pump seal life to more than 12 months. |
|
| Kalrez® Spectrum™ 7275 as the preferred elastomer for mechanical seals of pumps handling aggressive silanes and chlorosilanes. |
|
| While the incumbent FFKM O-ring showed signs of severe swelling and blistering, Kalrez® Spectrum™ 7275 seal had only superficial color change, with minimum swelling and unchanged flexibility. |
|
| Kalrez® Spectrum™ 7275 O-rings extended the Mean Time Between Repair (MTBR) of this mechanical seal by at least 30%. |
|
| Gross Weight | Net Weight | Carton Each | Carton Length | Carton Weight | Carton Height |
|---|---|---|---|---|---|
| 0 | 0 | 0 | |||
| 0 | 0 | 0 | |||
| 0 | 0 | 0 |
| Property | Value | Unit | Method |
|---|---|---|---|
| Color | - | — | Light Brown |
| Compression Set, 70 hrs. at 204 °C (400 °F) | ASTM D395B & D1414 (AS568 K214 O-ring test specimens) | % | 22 |
| 100% Modulus | ASTM D412 (Dumbbell test specimens) | MPa (psi) | 9.70 (1407) |
| Tensile Strength at Break | ASTM D412 (Dumbbell test specimens) | MPa (psi) | 14.50 (2103) |
| Lowest Service Temperature | DuPont proprietary test method; performance will vary with seal design and application specifics | °C (°F) | -20(-4) |
| Hardness | ASTM D2240 (Plied slab test specimens) | Shore A | 75 |
| Elongation at Break | ASTM D412 (Dumbbell test specimens) | % | 160 |
| Maximum Service Temperature | DuPont proprietary test method; performance will vary with seal design and application specifics | °C (°F) | 300 (572) |
|
Fabric/material |
MWO 7275 |
|---|---|
|
Design |
7275 |
|
Seam |
7275 |
|
Packaging |
7275 |
|
Hazard |
|
|
Coated Material |
MWO 7275 |
|
Features |
MEDIUM WHITE ORING |
|
Color |
WHITE |