Kalrez® perfluoroelastomer parts provide best in class chemical resistance for exploration and production services while also meeting the industry standard requirements.
Electrical properties |
|
Excellent broad chemical resistance & seal force retention in hot water/steam |
|
Suitable for use in sour service |
|
Compatible with amines found in drilling fluids, corrosion inhibitors, pump oil additives, etc. commonly used in the O&G industry |
|
Gross Weight | Net Weight | Carton Each | Carton Length | Carton Weight | Carton Height |
---|---|---|---|---|---|
0 | 0 | 0 | |||
0 | 0 | 0 | |||
0 | 0 | 0 |
Property | Value | Unit | Method |
---|---|---|---|
Tensile Strength at Break | ASTM D412 (Dumbbell test specimens) | MPa (psi) | 16.9 (2447) |
Elongation at Break | ASTM D412 (Dumbbell test specimens) | % | 128 |
Compression Set, 70 hrs. at 204 °C (400 °F) | ASTM D395B & D1414 (AS568 K214 O-ring test specimens) | % | 9 |
Compression Set, 70 hrs. at 260 °C (500 °F) | ASTM D395B & D1414 (AS568 K214 O-ring test specimens) | % | 15 |
Color | - | — | Black |
100% Modulus | ASTM D412 (Dumbbell test specimens) | MPa (psi) | 10.2 (1473) |
Hardness | ASTM D2240 (Plied slab test specimens) | Shore A | 79 |
Maximum Application Temperature | DuPont proprietary test method | °C (°F) | 300 (572) |
Fabric/material |
LBO 7375 |
---|---|
Design |
7375 |
Seam |
7375 |
Packaging |
7375 |
Hazard |
|
Coated Material |
LBO 7375 |
Features |
LARGE BLACK ORING |
Color |
BLACK |