Kalrez® perfluoroelastomer parts provide best in class chemical resistance for exploration and production services while also meeting the industry standard requirements.
| Outstanding erosion resistance to damaging Fluorine and Oxygen plasma radicals |
|
| Reduced total cost of ownership |
|
| Ultra-low particle generation |
|
| Exceptional thermal stability |
|
| Superb seal force retention properties |
|
| Excellent (low) compression set properties |
|
| Increased tool uptime and yield |
|
| Ultra-low outgassing |
|
| Gross Weight | Net Weight | Carton Each | Carton Length | Carton Weight | Carton Height |
|---|---|---|---|---|---|
| 0 | 0 | 0 | |||
| 0 | 0 | 0 | |||
| 0 | 0 | 0 |
| Property | Value | Unit | Method |
|---|---|---|---|
| Color | - | — | Olive Green |
| Compression Set, 70 hrs at 300 °C (572 °F) | ASTM D395B/D1414, (AS568A K214 O-ring test specimens) | % | 43 |
| Tensile Strength at Break | ASTM D412/D1414 (AS568A K214 O-ring test specimens) | MPa (psi) | 13.43 (1948) |
| Compression Set, 70 hrs at 204 °C (400 °F) | ASTM D395B/D1414, (AS568A K214 O-ring test specimens) | % | 15 |
| Hardness, Durometer | ASTM D2240 (Pellet test specimens) | Shore A | 70 |
| 100% Modulus | ASTM D412/D1414 (AS568A K214 O-ring test specimens) | MPa (psi) | 4.76 (690) |
| Elongation at Break | ASTM D412/D1414 (AS568A K214 O-ring test specimens) | % | 218 |
| Maximum Service Temperature | DuPont proprietary test method; performance will vary with seal design and application specifics | °C (°F) | 315 (600) |
|
Fabric/material |
CWS 9600 |
|---|---|
|
Design |
9600 |
|
Seam |
9600 |
|
Packaging |
9600 |
|
Hazard |
|
|
Coated Material |
CWS 9600 |
|
Features |
CUSTOM WHITE SHAPE |
|
Color |
WHITE |