DuPont™ Vespel® CP parts offer an array of fiber or fabric reinforced composites for a range of unique design needs when wear and strength are key. Composite parts can be found as replacements for aluminum or titanium in tube clamps. Wear strips are “self-lubricating”. Typically CP parts are used in aircraft bushings, wear pads, washers, bumpers and seals.
Vespel® CP-0644 composite parts consist of woven, carbon- fiber fabrics laminated in polyimide resin for strong, light, and durable components. CP parts are used as bushings and washers in high temperatures and oxidative environments.
| Gross Weight | Net Weight | Carton Each | Carton Length | Carton Weight | Carton Height |
|---|---|---|---|---|---|
| 0 | 0 | 0 | |||
| 0 | 0 | 0 | |||
| 0 | 0 | 0 |
| Property | Value | Unit | Method |
|---|---|---|---|
| Thermal Expansion Coefficienta | ASTM E-228-85 | m/m/°C (in/in/°F) | 43.2 x 10–6 (24 x 10–6 ) |
| Thermal Expansion Coefficient | ASTM D-696 | m/m/°C (in/in/°F) | 2.3 x 10–6 (1.3 x 10–6 ) |
| Glass Transition Temperature, Tg | Thermal Mechanical Analysis | °C (°F) | 360 (680) |
| TEST CONDITION – TDS-M202P (ULVAC) | — | — | 250(482) 10˚,10˚ 1.0(0.0022) 10-5/1.45 x 10-8 |
| DEFLECTION | — | — | 330 /44 x 106 230(446) |
| Property | Value | Unit | Method |
|---|---|---|---|
| Flexural Modulus | ASTM D-790 | MPa (ksi) | 21,000 (3,000) 17,000 (2,400) |
| Notched Izod | ASTM D-256 | J/m (ft·lb/in) | 171 (3.2) |
| Hardness, Rockwell 15-T | ASTM D-2240 | — | 79 |
| Ultimate Compressive Strengtha | ASTM D-3410 | MPa (ksi) | 140 (20) 100 (15) |
| Ultimate Flexural Strength | ASTM D-790 | MPa (ksi) | 220 (32) 165 (24) |
| Short-Beam Shear Strengtha | ASTM D-2344 | MPa (ksi) | 33 (4.8) 24 (3.5) |
| Tensile Modulus | ASTM D-638 | MPa (ksi) | 23,000 (3,400) 16,000 (2,300) |
| Compressive Modulusa | ASTM D-3410 | MPa (ksi) | 19,000 (2,700) 14,000 (2,100) |
| Ultimate Tensile Strength | ASTM D-638 | MPa (ksi) | 125 (18) 97 (14) |
| DENSITY | — | — | 1.70 106 |
| FINGER THICKNESS | — | — | 3 0.12 |
| TEST CONDITION – ASTM E595-93 | — | — | 0.329 0.002 |
| FLEXURAL MODULUS | — | — | 300 44 x 106 |
| FINGER WEIGHT | — | — | 0.50 1.10 |
|
Fabric/material |
VESPEL CP (POLYBON L) NR-150 BUSHING |
|---|---|
|
Design |
BUSHING |
|
Seam |
NR-150 (PI) |
|
Packaging |
BUSHING, D, D FLANGE |
|
Hazard |
|
|
Coated Material |
VESPEL CP (POLYBON L) NR-150 PARTS |
|
Features |
LAMINATE (MULTI-PLY) |